Influence of ion bombardment on growth and properties of PLD created DLC films |
|
| Authors: | Miroslav Jelínek Petr Písařík Tomáš Kocourek Josef Zemek Jaroslav Lukeš |
| Affiliation: | 1. Institute of Physics ASCR v.v.i., Na Slovance 2, 182 21, Prague 8, Czech Republic 2. Faculty of Biomedical Engineering, Czech Technical University in Prague, nám. Sítná 3105, 272 01, Kladno, Czech Republic 3. Faculty of Mechanical Engineering, Czech Technical University in Prague, Technicka 4, 166 07, Prague, Czech Republic |
| Abstract: | A hybrid PLD system with ion bombardment of films was developed. Growing DLC films were modified during the laser deposition (10 J?cm?2) by argon ions with energy in the range from 40 eV to 210 eV and cathode current of 0.15 A and 0.5 A. The content of sp2 “graphitic” and sp3 “diamond” bonds was measured using XPS. Sp3 bonds changed from 60 % to 81 %. We found the highest sp3 content for energy of 40 eV. Hardness (and reduced Young’s modulus) were determined by nanoindentation and reached 49 GPa (277 GPa). Film adhesion was studied using the scratch test and was up to 14 N for titanium substrates. Relations among deposition conditions and measured properties are presented. |
| Keywords: | |
| 本文献已被 SpringerLink 等数据库收录！ | |