Orthorhombic superstructures within the rare earth strontium-doped cobaltate perovskites: Ln1−xSrxCoO3−δ (Ln=Y, Dy-Yb; 0.750?x?0.875)

A combination of electron, synchrotron X-ray and neutron powder diffraction reveals a new orthorhombic structure type within the Sr-doped rare earth perovskite cobaltates Ln_1−xSr_xCoO_3−δ (Ln=Y³⁺, Dy³⁺, Ho³⁺, Er³⁺, Tm³⁺and Yb³⁺). Electron diffraction shows a C-centred cell based on a 2√2a_p×4a_p×4√2a_p superstructure of the basic perovskite unit. Not all of these very weak satellite reflections are evident in the synchrotron X-ray and neutron powder diffraction data and the average structure of each member of this series could only be refined based on Cmma symmetry and a 2√2a_p×4a_p×2√2a_p cell. The nature of structural and magnetic ordering in these phases relies on both oxygen vacancy and cation distribution. A small range of solid solution exists where this orthorhombic structure type is observed, centred roughly around the compositions Ln_0.2Sr_0.8CoO_3−δ. In the case of Yb³⁺ the pure orthorhombic phase was only observed for 0.850?x?0.875. Tetragonal (I4/mmm; 2a_p×2a_p×4a_p) superstructures were observed for compositions having higher or lower Sr-doping levels, or for compounds with rare earth ions larger than Dy³⁺. These orthorhombic phases show mixed valence (3+/4+) cobalt oxidation states between 3.2+ and 3.3+. DC magnetic susceptibility measurements show an additional magnetic transition for these orthorhombic phases compared to the associated tetragonal compounds with critical temperatures > 330 K.