La3Ru8B6 and Y3Os8B6, new members of a homologous series R(A)nM3n−1B2n

Two new compounds, La₃Ru₈B₆ and Y₃Os₈B₆, were synthesized by arc melting the elements. Their structural characterization was carried out at room temperature on as-cast samples by using X-ray diffractometry. According to X-ray single-crystal diffraction results these borides crystallize in Fmmm space group (no. 69), Z=4, a=5.5607(1) Å, b=9.8035(3) Å, c=17.5524(4) Å, ρ=8.956 Mg/m³, μ=25.23 mm⁻¹ for La₃Ru₈B₆ and a=5.4792(2) Å, b=9.5139(4) Å, c=17.6972(8) Å, ρ=13.343 Mg/m³, μ=128.23 mm⁻¹ for Y₃Os₈B₆. The crystal structure of La₃Ru₈B₆ was confirmed from Rietveld refinement of X-ray powder diffraction data. Both La₃Ru₈B₆ and Y₃Os₈B₆ compounds are isotypic with the Ca₃Rh₈B₆ compound and their structures are built up from CeCo₃B₂-type and CeAl₂Ga₂-type structural fragments taken in ratio 2:1. They are the members of structural series R(A)_nM_3n−1B_2n with n=3 (R is the rare earth metal, A the alkaline earth metal, and M the transition metal). Structural and atomic parameters were also obtained for La_0.94Ru₃B₂ compound from Rietveld refinement (CeCo₃B₂-type structure, P6/mmm space group (no. 191), a=5.5835(9) Å, c=3.0278(6) Å).