Composition-induced phase transition in Ca14Zn6−xGa10+xO35+x/2 (x=0.0 and 0.5)

Novel complex oxides Ca₁₄Zn₆Ga₁₀O₃₅ and Ca₁₄Zn_5.5Ga_10.5O_35.25 were prepared in air at 1200 °C, 72 h. Refinements of their crystal structures using X-ray powder diffraction data showed that Ca₁₄Zn₆Ga₁₀O₃₅ is ordered (S.G. F23, =0.0458, R_p=0.0485, R_wp=0.0659, χ²=1.88) and Ca₁₄Zn_5.5Ga_10.5O_35.25 disordered (S.G. F432, =0.0346, R_p=0.0601, R_wp=0.0794, χ²=2.82) variants of the crystal structure of Ca₁₄Zn₆Al₁₀O₃₅. In the crystal structure of Ca₁₄Zn₆Ga₁₀O₃₅, there are large empty voids, which could be partially occupied by additional oxygen atoms upon substitution of Zn²⁺ by Ga³⁺ as in Ca₁₄Zn_5.5Ga_10.5O_35.25. These oxygen atoms are introduced into the crystal structure of Ca₁₄Zn_5.5Ga_10.5O_35.25 only as a part of four tetrahedra (Zn, Ga)O₄ groups sharing common vertex. This creates a situation where even a minor change in the chemical composition leads to considerable anion and cation disordering resulting in a change of space group from F23 (no. 196) to F432 (no. 209).