Hydrothermal synthesis, thermal, structural, spectroscopic and magnetic studies of the Mn5−xCox(HPO4)2(PO4)2(H2O)4 (x=1.25, 2, 2.5 and 3) finite solid solution

The Mn_5−xCo_x(HPO₄)₂(PO₄)₂(H₂O)₄ (x=1.25, 2, 2.5, 3) finite solid solution has been synthesized by mild hydrothermal conditions under autogeneous pressure. The phases crystallize in the C2/c space group with Z=4, belonging to the monoclinic system. The unit-cell parameters obtained from single crystal X-ray diffraction are: a=17.525(1), b=9.0535(6), c=9.4517(7) Å, β=96.633(5) ° being R1=0.0436, wR2=0.0454 for Mn75Co25; a=17.444(2), b=9.0093(9), c=9.400(1) Å, β=96.76(1) ° being R1=0.0381, wR2=0.0490 for Mn60Co40; a=17.433(2), b=8.9989(9), c=9.405(1) Å, β=96.662(9) ° being R1=0.0438, wR2=0.0515 for Mn50Co50 and a=17.4257(9), b=8.9869(5), c=9.3935(5) Å, β=96.685(4) ° being R1=0.0296, wR2=0.0460 for Mn40Co60. The structure consists of a three dimensional network formed by octahedral pentameric entities (Mn,Co)₅O₁₆(H₂O)₆ sharing vertices with the (PO₄)³⁻ and (HPO₄)²⁻ tetrahedra. The limit of thermal stability of these compounds is, approximately, 165 °C, near to this mean temperature the phases loose their water content in two successive steps. IR spectra show the characteristic bands of the water molecules and the phosphate and hydrogen-phosphate oxoanions. The diffuse reflectance spectra are consistent with the presence of MO₆ octahedra environments in slightly distorted octahedral geometry, except for the M(3)O₆ octahedron which presents a remarkable distortion and so a higher Dq parameter. The mean value for the Dq and B-Racah parameter for the M(1),(2)O₆ octahedra is 685 and 850 cm⁻¹, respectively. These parameters for the most distorted M(3)O₆ polyhedron are 825 and 880 cm⁻¹, respectively. The four phases exhibit antiferromagnetic couplings as the major magnetic interactions. However, a small spin canting phenomenon is observed at low temperatures for the two phases with major content in the anisotropic-Co(II) cation.