Molecular weight distribution studies. I. Radiation-induced polymerization of liquid α-methylstyrene

The concentration of water in purified and BaO-dried α-methylstyrene was found to be 1.1 × 10^?4M. The radiation-induced bulk polymerization of the α-methylstyrene thus prepared was studied in the temperature range of ?20°C to 35°C. The polymerization rate varied as the 0.55 power of the dose rate. The theoretical molecular weights and molecular weight distribution were calculated from a proposed kinetic scheme and these values were then compared with those found experimentally. The agreement between these two was reasonably close, and therefore it was concluded that, from the molecular weight distribution point of view, the proposed kinetic scheme for the cationic polymerization of α-methylstyrene is an acceptable one. The rate constant for chain transfer to monomer k_f changed with temperature and was found to be responsible for the decrease in the molecular weight of the polymer with increase in temperature. k_f and k_p at 20°C were found to be 0.95 × 10⁴ l./mole-sec and 0.99 × 10⁶ l./mole-sec, respectively.