Transition Metal Atom Sites in Ternary ZrO2-TiO2-SiO2 Xerogels

There has been much work on the binary TiO₂-SiO₂ and ZrO₂-SiO₂ materials prepared by sol-gel because of the beneficial properties resulting from incorporation of Ti and Zr. In contrast the ternary TiO₂-ZrO₂-SiO₂ xerogels have been relatively little studied. We report the results of a study of those xerogels having Zr:Ti:Si ratios of 5:15:80, 10:10:80 and 15:5:80 heated to 750°C and to 1000°C. The study includes X-ray diffraction, small angle X-ray scattering, X-ray absorption spectroscopy at Ti and Zr K-edges, and ¹⁷O MAS-NMR. The study has benefited from close comparison with similar previous studies of the binary systems. The metal atoms in the ternary systems are shown to be predominantly homogeneously mixed in the silica network, as observed for the respective binary systems. The clear exception is for the sample with a minority of Zr, which after heat treatment at 750°C shows the presence of phase separation attributed to the formation of an amorphous precursor of ZrTiO₄; at 1000°C this phase crystallises. In samples with higher Zr content the crystallisation of a ZrO₂ tetragonal phase was observed. The data obtained illustrate well the strength of a research methodology in which a common batch of samples is studied using a coherent suite of modern structural probes.