Synthesis and Characterization of High Performance Poly(amide-imide)s based on a New Diimide-diacide and Various Diamines

A new diimide-diacid, (4-(4-(2,6-diphenylpyridin-4yl)phenoxy)phenyl)-1,3-bis(trimellitimidobenzene) (PPMIB), was synthesized from the condensation reaction of a new diamine, (4-(4-(2,6-diphenylpyridin-4yl)phenoxy)phenyl)-3,5-diaminobezamide (PPDA), and trimellitic anhydride carboxylic acid (TMAA) in glacial acetic acid. The diimide-diacid (PPMIB) was characterized by FT-IR, ¹H-NMR and elemental analysis. A series of novel aromatic poly(amide-imide)s (PAIs) was synthesized by using direct polycondensation of PPMIB with various diamines in NMP in the presence of triphenylposphite and pyridine as condensing agents. The resulting PAIs were amorphous, readily soluble in many polar aprotic solvents and showed inherent viscosities of 0.35–0.50 dL/g. According to thermal analysis, these polymers exhibited glass transition temperatures (T_gs) in the range of 202–280°C and temperature of 10% weight loss (T₁₀) varied from 400 to 545°C in N₂. These polymers in NMP solution exhibited strong UV-Vis absorption maxima at 320°C nm and their fluorescence emission peaks appeared around 410–565 nm.