Controlled Preparation and Reactive Silver‐Ion Sorption of Electrically Conductive Poly(N‐butylaniline)–Lignosulfonate Composite Nanospheres

Electroconductive poly(N‐butylaniline)–lignosulfonate (PBA–LS) composite nanospheres were prepared in a facile way by in situ, unstirred polymerization of N‐butylaniline with lignosulfonate (LS) as a dispersant and dopant. The LS content was used to optimize the size, structure, electroconductivity, solubility, and silver ion adsorptive capacity of the PBA–LS nanospheres. Uniform PBA–LS10 nanospheres with a minimal mean diameter of 375 nm and high stability were obtained when the LS content was 10 wt %. The PBA–LS10 nanospheres possess an increased electroconductivity of 0.109 S cm^?1 compared with that of poly(N‐butylaniline) (0.0751 S cm^?1). Furthermore, the PBA–LS10 nanospheres have a maximal silver‐ion sorption capacity of 815.0 mg g^?1 at an initial silver ion concentration of 50 mmol L ^?1 (25 °C for 48 h), an enhancement of 70.4 % compared with PBA. Moreover, a sorption mechanism of silver ions on the PBA–LS10 nanospheres is proposed. TEM and wide‐angle X‐ray diffraction results showed that silver nanoparticles with a diameter size range of 6.8–55 nm was achieved after sorption, indicating that the PBA–LS10 nanospheres had high reductibility for silver ions.