Atomic‐Level Alloying and De‐alloying in Doped Gold Nanoparticles

Atomically precise alloying and de‐alloying processes for the formation of Ag–Au and Cu–Au nanoparticles of 25‐metal‐atom composition (referred to as Ag_xAu_25?x(SR)₁₈ and Cu_xAu_25?x(SR)₁₈, in which R=CH₂CH₂Ph) are reported. The identities of the particles were determined by matrix‐assisted laser desorption ionization mass spectroscopy (MALDI‐MS). Their structures were probed by fragmentation analysis in MALDI‐MS and comparison with the icosahedral structure of the homogold Au₂₅(SR)₁₈ nanoparticles (an icosahedral Au₁₃ core protected by a shell of Au₁₂(SR)₁₈). The Cu and Ag atoms were found to preferentially occupy the 13‐atom icosahedral sites, instead of the exterior shell. The number of Ag atoms in Ag_xAu_25?x(SR)₁₈ (x=0–8) was dependent on the molar ratio of Ag^I/Au^III precursors in the synthesis, whereas the number of Cu atoms in Cu_xAu_25?x(SR)₁₈ (x=0–4) was independent of the molar ratio of Cu^II/Au^III precursors applied. Interestingly, the Cu_xAu_25?x(SR)₁₈ nanoparticles show a spontaneous de‐alloying process over time, and the initially formed Cu_xAu_25?x(SR)₁₈ nanoparticles were converted to pure Au₂₅(SR)₁₈. This de‐alloying process was not observed in the case of alloyed Ag_xAu_25?x(SR)₁₈ nanoparticles. This contrast can be attributed to the stability difference between Cu_xAu_25?x(SR)₁₈ and Ag_xAu_25?x(SR)₁₈ nanoparticles. These alloyed nanoparticles are promising candidates for applications such as catalysis.