Fluorene‐rich high performance polyesters: Synthesis and characterization of 9,9‐fluorenylidene and 2,7‐fluorenylene‐based polyesters with excellent optical property |
| |
| Authors: | Surasak Seesukphronrarak Shinichi Kawasaki Kana Kobori Toshikazu Takata |
| |
| Institution: | 1. Department of Organic and Polymeric Materials, Tokyo Institute of Technology, Ookayama, Meguro‐ku, Tokyo 152‐8552, Japan;2. Advanved Material Business Promotion Department, Osaka Gas Co., Ltd., Konohana‐ku, Osaka 554‐0051, Japan |
| |
| Abstract: | Polyesters PEs containing high content of fluorene units in their backbones were synthesized from 9,9‐diarene‐substituted fluorene diols ( 1 ) and fluorene‐based diacid chlorides ( 2 ) by high temperature polycondensation at 185 °C in diphenyl ether. The molecular weights of the polyesters PE1‐PE5 were in a range of Mw 25,000–165,000. The polyesters displayed their high thermostability: the glass transition temperatures (Tg) by differential scanning calorimetry analysis ranged from 109 to 217 °C, while the 10% weight loss temperatures (Td10) measured by thermogravimetric analysis were over 400 °C in nitrogen and 395 °C in air. The polyesters had good solubility in most common organic solvents such as chloroform and toluene and gave tough, transparent and flexible cast films. The transmittance of the films was over 80% in the wavelength range from 450 to 700 nm in any PEs . The PEs exhibited high refractive index values around 1.65, while they had very low degree of birefringence. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 2549–2556, 2008 |
| |
| Keywords: | polyaromatics polyesters refractive index transparency |
|
|