Vinyl addition polymerization of norbornene using cyclopentadienylzirconium trichloride activated by isobutyl‐modified methylaluminoxane

Norbornene polymerization using the commercially available and inexpensive catalyst system, cyclopentadienylzirconium trichloride (CpZrCl₃) and isobutyl‐modified methylaluminoxane (MMAO), were carried out over a wide range of polymerization temperatures and monomer concentrations. For the CpZrCl₃ catalyst system activated by aluminoxane with a 40 mol % methyl group and a 60 mol % isobutyl group (MMAO_40/60), the polymerization temperature and monomer concentration significantly affected the molecular weight (M_n) of the obtained polymer and the catalytic activity. With an increase in the polymerization temperature from 0 to 27 °C, the catalytic activity and M_n increased, but these values dramatically decreased with the increasing polymerization temperature from 27 to 70 °C, meaning that the most suitable temperature was 27 °C. The CpZrCl₃/MMAO_40/60 (Al]/Zr] = 1000) catalyst system with the NB] of 2.76 mol L^?1 at 27 °C showed the highest activity of 145 kg mol_Zr^?1 h^?1 and molecular weight of 211,000 g mol^?1. The polymerization using the CpZrCl₃/MMAO_40/60 catalyst system proceeds through the vinyl addition mechanism to produce atactic polynorbornene, which was soluble in chloroform, toluene, and 1,2‐dichlorobenzene, but insoluble in methanol. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 1185–1191, 2008