Preparation of single-crystalline ZnO films on ZnO-buffered a-plane sapphire by chemical bath deposition

High-quality zinc oxide (ZnO) films were successfully grown on ZnO-buffered a-plane sapphire (Al₂O₃ (1 1 2¯ 0)) substrates by controlling temperature for lateral growth using chemical bath deposition (CBD) at a low temperature of 60 °C. X-ray diffraction analysis and transmission electron microscopy micrographs showed that the ZnO films had a single-crystalline wurtzite structure with c-axis orientation. Rocking curves (ω-scans) of the (0 0 0 2) reflections showed a narrow peak with full width at half maximum value of 0.50° for the ZnO film. A reciprocal space map indicated that the lattice parameters of the ZnO film (a=0.3250 nm and c=0.5207 nm) were very close to those of the wurtzite-type ZnO. The ZnO film on the ZnO-buffered Al₂O₃ (1 1 2¯ 0) substrate exhibited n-type conduction, with a carrier concentration of 1.9×10¹⁹ cm⁻³ and high carrier mobility of 22.6 cm² V⁻¹ s⁻¹.