Elastic moduli and structure of low density polyethylene

Summary Low density polyethylene film is drawn at room temperature four times the original length and subjected to thermal annealing at 60, 80, and 100 °C keeping the film length constant. Long spacing measured by SAXS increased with increasing temperature of annealing; the increase of the long spacing is presumed to be due to the decrease of the number of micelles through relaxation during the annealing. Simultaneous measurement of the changes of the long spacing and the film length by stretching is carried out and stress-extension curves are obtained. The values of the initial moduli of the long spacingE ₁ and the film lengthY are very near to each other. Elastic modulus of the crystal latticeE _c is known to be 235 GN/m² and that of the amorphous regionE _a is found to be 0.15 GN/m². When higher stress is applied than in the case of the initial modulus, the percentage of extension of film is much greater than that of the long spacing. The discrepancy is explained by the increase of the number of micelles through stress crystallization.Dedicated to Professor Dr. K. Ueberreiter on the occasion of his 70th birthday.