掺Co钨酸镉单晶体的坩埚下降生长及光谱特性

应用坩埚下降法,采用70℃.cm-1的固液界面温度梯度与0.50 mm.h-1生长速度,生长出了初始Co掺杂摩尔百分浓度为0.5 mol%、尺寸为Ф25 mm×120 mm的钨酸镉单晶体。晶体呈透明深蓝色。用XRD表征了获得的晶体。观测到518,564和655 nm三个可见波段吸收带以及发光中心1 863 nm(1 323～2 220 nm)的超宽吸收带。可见波段的吸收归属于Co2+在八面晶格场中4T1(4F)→4A2(4F),4T1(4F)→4T1(4P)跃迁叠加,而红外波段的宽带吸收则为八面体场Co2+的4T1(4F)→4T2(4F)能级跃起所致。从吸收特性表明,Co离子掺杂于畸变的氧八面体中,呈现+2价态。根据吸收光谱计算出晶格场参数Dq=990 cm-1,Racah参数BC=726.3 cm-1。在520 nm波长光的激发下,观察到778 nm波段的荧光发射,归属于八面体晶格场中Co2+的4T1(4P)→4T1(4F)能级的跃迁。从吸收与荧光强度的变化推断:沿着晶体生长方向,Co2+浓度逐渐增加,有效分凝系数小于1。

Growth of codoped CdWO4 crystals by Bridgman method and their optical spectra

The CdWO4 crystals with good quality in the size of Phi25 mm x 120 mm, doped with Co in 0.5% molar fraction in the raw composition, were grown by the Bridgman method by taking -70 degrees C x cm(-1) of solid-liquid interface and -0.50 mm x h(-1) growth rate. The crystal presents transparence and deep blue. The X-ray diffraction (XRD) was used to characterize the crystals. Three absorption peaks at 518, 564 and 655 nm respectively, which are attributed to the overlapping of 4 T1 (4F) --> 4A2 (4F) and 4 T1 (4F) --> 4 T1 (4P) of Co2+ octahedrons, and a wide band centered at 1 863 nm, which is attributed to 4Ti (4F) --> 4 T2 (4F), was observed. The absorption results indicated that the Co ions presented +2 valence in crystal and located within the distorted oxygen octahedrons. The crystal-field parameter D(q) and the Racah parameter B were estimated to be 990 and 726.3 cm(-1) respectively based on the absorption spectra. A fluorescence emission at 778 nm (4T1 (4P) --> 4 T1 (4F)) for codoped CdWO4 crystals was observed under excitation by 520 nm light. It can be deduced from the changes in absorption and emission intensity of different parts of crystal that the concentration of Co2+ ion in crystal increased along growing direction and the effective distribution coefficient of Co2+ ion in CdWO4 crystal is less than 1.