Preparation,copolymerization kinetics,and viscoelastic behavior of copolymers of 1,3-butadiene and 1,4-diphenyl-1,3-butadiene

1,4-Diphenyl-1,3-butadiene reacts readily with sec-butyllithium in toluene to form adducts. Although this 1,4-substituted conjugated diene did not homopolymerize or copolymerize with styrene, with butadiene it formed copolymers having compositions varying from one end of the chain to the other. The monomer reactivity ratios found were r₁ = 8.2, r₂ = 0 in toluene and r₁ = 2.1, r₂ = 0 in toluene–tetrahydrofuran (0.2%) solution. The intramolecular composition distribution of these polymers varied from an initial butadiene-rich composition, dependent on the ratio of monomers charged, to the equimolar composition of the alternating copolymer. In spite of this compositional heterogeneity, the crosslinked polymers exhibited a single glass transition characteristic of the mean composition. A secondary, high-temperature dispersion observed in the dynamic viscoelastic properties of some of the products is shown to be attributable to network topological effects.