Copolymerization of norbornene and 5‐norbornene‐2‐yl acetate using novel bis(β‐ketonaphthylamino)Ni(II)/B(C6F5)3/AlEt3 catalytic system

Vinyl‐type copolymerization of norbornene (NBE) and 5‐NBE‐2‐yl‐acetate (NBE‐OCOMe) in toluene were investigated using a novel homogeneous catalyst system based on bis(β‐ketonaphthylamino)Ni(II)/B(C₆F₅)₃/AlEt₃. The copolymerization behavior as well as the copolymerization conditions, such as the levels of B(C₆F₅)₃ and AlEt₃, temperature, and monomer feed ratios, which influence on the copolymerization were examined. Without combination of AlEt₃, the catalytic bis(β‐ketonaphthylamino)Ni(II)/B(C₆F₅)₃ exhibited very high catalyst activity for polymerization of NBE. Combination of AlEt₃ in catalyst system resulted in low conversion for polymerization of NBE. For copolymerization of NBE and NBE‐OCOMe, involvement of AlEt₃ in catalyst is necessary. Slight addition of NBE‐OCOMe in copolymerization of NBE and NBE‐OCOMe gives rise to significant increase of catalyst activity for catalytic system bis(β‐ketonaphthylamino)Ni(II)/B(C₆F₅)₃/AlEt₃. Nevertheless, excess increase of the NBE‐OCOMe content in the comonomer feed ratios results in decrease of conversion as well as activity of catalyst. The achieved copolymers were confirmed to be vinyl‐addition copolymers through the analysis of FTIR, ¹H NMR, and ¹³C NMR spectra. ¹³C NMR studies further revealed the composition of the copolymer and the incorporation rate was 7.6–54.1 mol % ester units at a content of 30–90 mol % of the NBE‐OCOMe in the monomer feeds ratios. TGA analysis results showed that the copolymer exhibited good thermal stability (T_d > 410 °C) and failed to observe the glass transitions temperature over 300 °C. The copolymers are confirmed to be noncrystalline by WAXD analysis results and show good solubility in common organic solvents. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 3990–4000, 2009