Magnetic and structural studies of the alloy system REIn0.5Ag0.5

The structural and magnetic properties of the alloy system REIn_0.5Ag_0.5 RE = Gd, Tb, Dy, Ho, Er, Tm and Yb] are reported. All these alloys (except that of Yb) crystallize in a cubic CsCl type structure at room temperature. Low temperature X-ray diffraction data does not reveal any structural phase transformation down to 8 K. On the basis of magnetic susceptibility data at a different temperature (3–300 K) and applied magnetic field (2 × 10⁵ to 8 × 10⁶ A m^-1, it has been concluded that GdIn_0.5Ag_0.5 is ferromagnetic (T_c = 118 K), TbIn_0.5Ag_0.5 and DyIn_0.5Ag_0.5 are meta magnetic (T_N = 66 and 30 K, respectively) and alloys involving Ho, Er, Tm and Yb are ferrimagnetic with Néel temperatures (T_N) equal to 24, 22, 21 and 20 K, respectively. The evaluated effective magneton number (p) is found to be slightly larger compared to theoretical values for tripositive ions of Gd, Tb and Dy and a bit smaller for Ho, Er, Tm and Yb. The results have been qualitatively explained using appropriate theories.