Synthesis of chromium silicide with laser pulses

Thin chromium films, 60 nm thick, were deposited onto single-crystal silicon wafers. The samples were irradiated with 30 ns single pulses from a Nd: glass laser at fluences ranging from 0.4 to 2.25 J/cm². Rutherford backscattering spectrometry, transmission electron microscopy and electron diffraction measurements evidence the formation of CrSi₂ layers at the Cr/Si interface. The silicide thickness depends on the laser fluence.