Reactive plasma cladding of TiC/Fe cermet coating using asphalt as a carbonaceous precursor |
|
| Authors: | Junbo Liu Limei Wang |
| Institution: | a School of Mechanical and Electronic Engineering, Weifang University, Weifang 261061, China b School of Information and Control Engineering, Weifang University, Weifang 261061, China c School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China |
| Abstract: | A new process of preparing Ti-Fe-C composites powder for reactive plasma cladding, precursor carbonization-composition process, was developed. TiC/Fe cermet coatings were synthesized by reactive plasma cladding of the composite powder. XRD and SEM were employed to analyze the phase composition and microstructure of the composite powder and coating. The hardness and wear resistance of the coating was tested. Results show that: The compound powder prepared by precursor carbonization-composition process has very tight structure, which can avert the question of raw powder breaking-up in cladding process. The TiC/Fe cermet coating by reactive plasma cladding consists of alternate, laminated layers as following: the layers in which the round nanoscale TiC particles are dispersed within the α-Fe matrix and the layers of TiC accumulation. The TiC/Fe cermet coating by reactive plasma cladding shows superior hardness and wear resistance: The surface hardness of the TiC/Fe cermet coating is 68 ± 6 (HR30 N). In the same fretting conditions, the wear resistance of Ni60 coating is twelve times than that of the TiC/Fe cermet coating. |
| Keywords: | Cermet coating Reactive plasma cladding TiC/Fe Precursor |
| 本文献已被 ScienceDirect 等数据库收录！ | |