The electrical properties of dielectric stacks of SiO2 and Al2O3 prepared by atomic layer deposition method

We produced dielectric stacks composed of ALD SiO₂ and ALD Al₂O₃, such as SiO₂/Al₂O₃, Al₂O₃/SiO₂, and SiO₂/Al₂O₃/SiO₂, and measured the leakage currents through the stacks in comparison with those of the single oxide layers. SiO₂/Al₂O₃ shows lowest leakage current for negative bias region below 6.4 V, and Al₂O₃/SiO₂ showed highest current under negative biases below 4.5 V. Two distinct electron conduction regimes are observed for Al₂O₃ and SiO₂/Al₂O₃. Poole-Frenkel emission is dominant at the high-voltage regime for both dielectrics, whereas the direct tunneling through the dielectric is dominant at the low-voltage regime. The calculated transition voltage between two regimes for SiO₂ (6.5 nm)/Al₂O₃ (12.6 nm) is −6.4 V, which agrees well with the experimental observation (−6.1 V). For the same EOT of entire dielectric stack, the transition voltage between two regimes decreases with thinner SiO₂ layer.