Non-random cation distribution in hexagonal Al0.5Ga0.5PO4

Based on powder X-ray diffraction and ³¹P Magic Angle Spinning Nuclear Magnetic Resonance (MAS NMR) investigations of mixed phosphate Al_0.5Ga_0.5PO₄, prepared by co-precipitation method followed by annealing at 900 °C for 24 h, it is shown that Al_0.5Ga_0.5PO₄ phase crystallizes in hexagonal form with lattice parameter a=0.491(2) and c=1.106(4) nm. This hexagonal phase of Al_0.5Ga_0.5PO₄ is similar to that of pure GaPO₄. The ³¹P MAS NMR spectrum of the mixed phosphate sample consists of five peaks with systematic variation of their chemical shift values and is arising due to existence of P structural units having varying number of the Al³⁺/Ga³⁺ cations as the next nearest neighbors in the solid solution. Based on the intensity analysis of the component NMR spectra of Al_0.5Ga_0.5PO₄, it is inferred that the distribution of Al³⁺ and Ga³⁺ cations is non-random for the hexagonal Al_0.5Ga_0.5PO₄ sample although XRD patterns showed a well-defined solid solution formation.