Synthesis, structural determination and magnetic properties of layered hybrid organic-inorganic, iron (II) propylphosphonate, Fe[(CH3(CH2)2PO3)(H2O)], and iron (II) octadecylphosphonate, Fe[(CH3(CH2)17PO3)(H2O)]

Fe[(CH₃(CH₂)₂PO₃)(H₂O)] (1) and Fe[(CH₃(CH₂)₁₇PO₃)(H₂O)] (2) were synthesized by reaction of FeCl₂·6H₂O and the relevant phosphonic acid in water in presence of urea and under inert atmosphere. The compounds were characterized by elemental and thermogravimetric analyses, UV-visible and IR spectroscopy. The crystal structure of (1) was determined from X-ray single crystal diffraction studies at room temperature: monoclinic symmetry, space group P2₁, , , , and β=98.62(3)°. The compound is lamellar and the structure is hybrid, made of alternating inorganic and organic layers along the c direction. The inorganic layers consist of Fe(II) ions octahedrally coordinated by five phosphonate oxygen atoms and one from the water molecule, separated by bi-layers of propyl groups. A preliminary structure characterization of compound (2) suggests a similar layered structure, but with an interlayer spacing of 40.3 Å. The magnetic properties of the compounds were both studied by a dc and ac SQUID magnetometer. Fe[(CH₃(CH₂)₂PO₃)(H₂O)] (1) obeys the Curie-Weiss law at temperatures above 50 K (, ), indicating a Fe +II oxidation state, a high-spin d⁶ (S=2) electronic configuration and an antiferromagnetic exchange couplings between the near-neighbouring Fe(II) ions. Below , Fe[(CH₃(CH₂)₂PO₃)(H₂O)] exhibits a weak ferromagnetism. The critical temperature of has been determined by ac magnetic susceptibility measurements. Compound (2) shows the same paramagnetic behaviour of the iron (II) propyl derivative. The values of C and θ were found to be and −44 K, respectively, thus suggesting the presence of Fe +II ion in the S=2 spin state and antiferromagnetic interactions between Fe(II) ions at low temperatures. Zero-field and field cooled magnetic susceptibility vs. T plots do not overlap below , suggesting the presence of an ordered magnetic state. The critical temperature, T_N, has been located by the peaks at from the ac susceptibility (χ′and χ″) vs. T plots. Below T_N hysteresis loops recorded in the temperature region show an S-shape, while below 15 K assume an ellipsoid form. They reveal that compound (2) is a weak ferromagnet. The critical temperature T_N in these layered Fe(II) alkylphosphonates is independent of the distance between the inorganic layers.