Synthesis and photoluminescence characteristics of (Sr, Ca)3B2O6:Eu for application in white light-emitting diodes

A series of yellow-green (Sr, Ca)₃B₂O₆:Eu phosphors have been synthesized using precursors prepared via a facile sol-gel route. The solid-solution phases crystallized to materials with the formula of Sr_3−x−yCa_xEu_yB₂O₆ with varied Ca²⁺ and Eu²⁺ contents. The emission peak centered at 540 nm under near-UV excitation exhibited a broad-band distribution in the range of 450-650 nm. The dependences of the luminescence intensity on the contents of Ca²⁺ substitution and Eu²⁺ dopant were also investigated. The composition in the host lattice sensitively affected the chromaticity index. Sr_1.21Ca_1.7Eu_0.09B₂O₆ (SCB:0.09Eu) was shown to possess the highest intensity and broadest emission band. Calcining temperature was shown to greatly influence the luminescent properties of SCB:0.09Eu. It is concluded that SCB:0.09Eu can be used as an efficient yellow-green phosphor for white light-emitting diodes (white LEDs) applications.