Conducting Graphene Decorated Li3V2(PO4)3/C for Lithium‐Ion Battery Cathode with Superior Rate Capability and Cycling Stability

In this study, core‐shell structured Li₃V₂(PO₄)₃/C wrapped in graphene nanosheets has been successfully prepared. The reduction of graphene oxide and the synthesis of Li₃V₂(PO₄)₃/C are carried out simultaneously using a chemical route followed by a solid‐state reaction. The effects of conducting graphene are studied by X‐ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Raman spectra and electrochemical measurements. The results reveal that the graphene sheets not only form a compact and uniform coating layer throughout the Li₃V₂(PO₄)₃/C, but also stretch out and cross‐link into a conducting network around the Li₃V₂(PO₄)₃/C particles. Thus, the graphene decorated Li₃V₂(PO₄)₃/C electrode exhibits superior high‐rate capability and long‐cycle stability. It delivers a reversible discharge capacity of 178.2 mAh·g^?1 after 60 cycles at a current density of 0.1 C, and the rate performances of 176, 169.3, 156.1 and 135.7 mAh·g^?1 at 1, 2, 5 and 10 C, respectively. The superior electrochemical properties make the graphene decorated Li₃V₂(PO₄)₃/C composite a promising cathode material for high‐performance lithium‐ion battery.