Chain dimensions in plastically deformed semicrystalline polymers

The effect of plastic deformation on the chain dimensions of polymers in the semicrystalline state was investigated using linear hydrogenated polybutadiene (HPB), a model ethylene/butene-1 copolymer having about 40% crystallinity at room temperature. Dilute blends of deuterium-labeled chains with various molecular weights (20,000 ≤ M ≤ 214,000) in the same unlabeled matrix (M = 95,000) were uniaxially stretched at 25°C to extension ratios of α = 2.4 and 4.4. Radius of gyration normal to the stretch direction R_⊥ was measured for the labeled chains by small-angle neutron scattering. The molecular extension ratio inferred from these data α_m = R/R was significantly smaller than α for short chains (M < 50,000) but increased to the affine range α_m = α for M > 100,000. This variation in α_m/α closely parallels the molecular weight dependence of mechanical strength and ductility in HPB over the same range.