Sunlight photocatalytic activity of CdS modified TiO2 loaded on activated carbon fibers

To improve the photocatalytic application performances of TiO₂, in this work, firstly CdS modified Degussa P25 TiO₂ (CdS/TiO₂) composites were prepared by two methods, sol-gel method and precipitation method. Next they, sol-gel-CdS/TiO₂ (sg-CdS/TiO₂) and precipitation-CdS/TiO₂ (pp-CdS/TiO₂), were loaded on activated carbon fibers (ACFs) by dip-coating method using the sodium carboxymethyl cellulose as adhesives. The composites were characterized by XRD, UV-vis absorbance spectra, SEM, EDS and BET. The photocatalytic activities under sunlight were investigated by the degradation of methylene blue. The results showed that CdS/TiO₂ composites were mainly composed of anatase-TiO₂ and little CdS cubic phases. The absorption wavelengths of sg-CdS/TiO₂ and pp-CdS/TiO₂ composites were extended to 590 nm and 740 nm, respectively. The absorption edge had a pronounced ‘red shift’. From EDS analysis, the elemental contents of CdS/TiO₂ were mainly Ti and O and a small quantity of S and Cd. CdS/TiO₂ loaded on ACFs were in the form of small clusters, but not very uniform; compared with the original ACFs, the surface area and pore volume of CdS/TiO₂/ACFs decreased slightly, respectively, while the average pore diameter was not changed. The photodegradation rate of methylene blue under sunlight with CdS/TiO₂/ACFs composites was markedly higher than that of P25-TiO₂/ACFs, and the effect of pp-CdS/TiO₂/ACFs composites was better than that of sg-CdS/TiO₂/ACFs, when irradiated for 180 min, and the photodegradation rate of methylene blue reached to 90.1%. The photodegradation kinetics of the methylene blue fitted with the Langmuir-Hinshelwood equation. The apparent reaction rate constants of sg-CdS/TiO₂/ACFs and pp-CdS/TiO₂ were 0.0105 min⁻¹ and 0.0146 min⁻¹, respectively, which were about 1.3-1.7 times as large as that of P25-TiO₂/ACFs.