| 具有不同Bi/Ti摩尔比的BiOI/TiO2 (A)光催化剂的结构与性能 |
| |
| 引用本文： | 李慧泉,崔玉民,吴兴才,华林,洪文珊.具有不同Bi/Ti摩尔比的BiOI/TiO2 (A)光催化剂的结构与性能[J].物理化学学报,2012,28(8):1985-1991. |
| |
| 作者姓名： | 李慧泉 崔玉民 吴兴才 华林 洪文珊 |
| |
| 作者单位： | 1. School of Chemistry and Chemical Engineering, Fuyang Normal College, Fuyang, 236041, Anhui Province, P. R. China;
2. Anhui Provincical Key Laboratory for Degradation and Monitoring of Pollution of the Environment, Fuyang 236041, P. R. China;
3. The State Key Laboratory of Coordination Chemistry, Nanjing University, Nanjing 210093, P. R. China;
4. R&D center, Singapore Linovus Technology Pte Ltd, 059818, Singapore |
| |
| 基金项目： | supported by the National Natural Science Foundation of China (21171091);Natural Science Foundation of Higher Education Institutions in Anhui Province,China (KJ2012A217,KJ2012B136)~~ |
| |
| 摘 要： | 在室温条件下通过沉积法制备了BiOI敏化纳米锐钛矿TiO2 (A)光催化剂. 用X射线衍射(XRD),X射线光电子能谱(XPS), 光致发光(PL)光谱和紫外-可见漫反射(UV-Vis DRS)等手段对其进行了表征. 通过罗丹明B(RhB)催化降解实验评价了其光催化活性. 随BiOI含量增加, BiOI/TiO2 (A)在370-630 nm的吸收强度增强, 吸收带边红移增加, 紫外和可见光催化活性先增加, 当BiOI含量约为1.7% (质量分数)时, 各自达到最大值, 然后随BiOI含量的进一步增加而减小. 1.7% BiOI/TiO2 (A)的可见光活性明显高于P25, 它的紫外光活性也略高于P25. 在BiOI含量相近时, BiOI/TiO2 (A)比BiOI/P25具有更低的光催化活性. 和TiO2 (A)相比, 1.7% BiOI/TiO2 (A)明显具有更高的紫外和可见光催化活性, 这归功于它在370-630 nm的强吸收、吸收带边红移明显以及光生电子和空穴的有效转移, 减少了电子-空穴对的复合.
|
| 关 键 词： | 沉积法 敏化 锐钛矿 BiOI含量 光催化 |