Radiation-induced,solid-state polymerization of derivatives of methacrylic acid. I. Postirradiation polymerization of zinc methacrylate

The postirradiation polymerization of the crystalline, anhydrous, monohydrate, and dihydrate forms of zinc methacrylate was studied. The anhydrous salt polymerized readily in the temperature range 50–150°C., the monohydrate did not polymerize at all, and the dihydrate polymerized at about 100°C. Aging of the anhydrous salts greatly affected the rate of polymerization; this was shown to be due mainly to the formation of peroxides by reaction with air. Polymerization could be initiated thermally, without irradiation, in monomer which had been aged in contact with air, apparently by decomposition of the peroxides. The rate of the postirradiation polymerization was increased when air was present during irradiation and decreased when air was present during polymerization. The rate of polymerization increased with temperature, corresponding to an apparent activation energy of 10 kcal./mole. The dihydrate lost one molecule of water rapidly under vacuum at 20°C. and slowly on heating at 50°C. in a sealed vessel, forming a crystalline monohydrate. Slow thermal polymerization and rapid postirradiation polymerization occurred at 100°C. without the formation of any monohydrate, indicating that the polymerization was concurrent with the phase change.