AlF3 coating of LiNi0.5Mn1.5O4 for high-performance Li-ion batteries
Authors:Jiangang Li  Yayuan Zhang  Jianjun Li  Li Wang  Xiangming He  Jian Gao
Affiliation:(1) Institute of Nuclear & New Energy Technology, Tsinghua University, Beijing, 100084, People’s Republic of China;(2) Beijing Institute of Petrochemical Technology, Beijing, 102617, People’s Republic of China;
Abstract:AlF3-coating is attempted to improve the performance of LiNi0.5Mn1.5O4 cathode materials for Li-ion batteries. The prepared powders are characterized by scanning electron microscope, powder X-ray diffraction, charge/discharge, and impedance. The coated LiNi0.5Mn1.5O4 samples show higher discharge capacity, better rate capability, and higher capacity retention than the uncoated samples. Among the coated samples, 1.0 mol% AlF3-coated sample shows highest capacity after charge–discharged at 30 mA/g for 3 cycles, but 4.0 mol% coated sample exhibits the highest capacity and cycling stability when cycled at high rate of 150 and 300 mA/g. The 40th cycle discharge capacity at 300 mA/g current still remains 114.8 mAh/g for 4.0 mol% AlF3-coated LiNi0.5Mn1.5O4, while only 84.3 mAh/g for the uncoated sample.
Keywords:
本文献已被 SpringerLink 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号