Structural analysis of Cd-Te-O films prepared by RF reactive sputtering

Crystalline and microcrystalline Cd-Te-O samples have been obtained by RF reactive sputtering from a CdTe target using N₂O as oxidant. The growth conditions were substrate temperatures of 323 K, 573 K and 773 K and cathode voltage of −400 V, corresponding to 30 W of forward power. The samples were studied by micro-Raman spectroscopy, X-ray diffraction and optical transmittance. The films are remarkably transparent in the visible range, with transmittances about 88% at 400 nm and band gap energies above the absorption edge of the glass substrates. Although only the samples prepared at 773 K present defined diffraction peaks, the analysis of the Raman spectra indicate that samples prepared at 323 K and 573 K have a defined microstructure indeed. The spectra fitting performed by comparison with pattern compounds demonstrate that Cd-Te-O films are formed of Te-O units similar to those present in metal oxide-doped tellurite glasses, such as TeO₃ and TeO_3 + 1 linked through Cd-O bonds. As the substrate temperature increases the microstructure evolves from a γ-TeO₂ richer state to Cd_xTe_yO_z. In the crystalline sample the main phase identified was CdTeO₃ even though evidence of other phases was observed.