Magnetostructural transformations in Ni51Mn36Sn13 Heusler alloy thin films

In this paper we report structural, magnetic and transport properties of strongly textured Ni₅₁Mn₃₆Sn₁₃ thin films. The off-stoichiometric Heusler alloy films with 200 nm thickness were sputter-deposited on a MgO(100) substrate at 500 K and after annealed at 1000 K in UHV conditions. The textured growth was confirmed by x-ray diffraction in Bragg-Brentano geometry. The temperature dependence of the magnetic properties was measured by VSM and FMR methods. The electron transport measurements were carried out in function of temperature in 0 Oe and 50 kOe fields. All measurements corroborate the existence of the martensitic transformation in the film. Furthermore, transport measurements reveal an influence of the magnetic field on the transition temperature.