Investigation of photo‐oxidative effect on morphology and degradation of mechanical and physical properties of nano CaCO3 silicone rubber composites

Photo‐oxidative degradation of treated and untreated nano CaCO₃: silicone rubber composite was studied under accelerated UV irradiation (≥290 nm) at different time intervals. Prolonged exposure to UV leads to a progressive decrease in mechanical and physical properties along with the change in behavior of filler‐matrix interaction. This was due to decrease in cross‐linking density with increase in mobility of rubber chains. Meanwhile, synthesized nano CaCO₃ was modified with stearic acid for uniform dispersion in rubber matrix. The increase in carbonyl (>CO), hydroxyl (? OH), CO₂, and alkene functional groups on the UV exposed surface of treated and untreated nano CaCO₃: silicone rubber composites at different time intervals was studied using Fourier transform infrared (FTIR) spectroscopy. The change in morphological behavior of filler‐matrix interaction after UV exposure was studied using SEM. Overall, the study showed that the treated nano CaCO₃: silicone composites were affected more by UV exposure than untreated nano CaCO₃: silicone composites and pristine composite after UV exposure. This effect was due to peeling of stearic acid from the surface of CaCO₃, which makes the rubber chains slippery and thus separation of filler and rubber chains takes place with initiation of fast‐degradation. Copyright © 2011 John Wiley & Sons, Ltd.