Preparation and characterization of silicate gel glasses containing Cr2O3

The effect of thermal treatment on the structural incorporation of Cr₂O₃ in xCr₂O₃·(100 – x)SiO₂ and 5R _n O·xCr₂O₃·(95 – x)SiO₂ (where x=0.01–1 mol.% and R=Li, Na and Ca) gel glasses was studied by optical absorption spectrophotometry, DTA-TG, XRD and electron microscopy.Samples heat treated at 60°C have green color due to the presence of Cr³⁺ in octahedral coordination. The optical transmission, and color (yellow, orange or ambar), of the samples heat treated between 200 and 700°C prove that Cr³⁺ (octahedrally coordinated) and Cr⁶⁺ (tetrahedrally coordinated) are both present. Segregation of Cr₂O₃ take place at temperatures above 800°C.In reducing conditions the gel glasses were green due to the presence of a high content of Cr³⁺ ions. Samples containing Li or Na show crystalline phases at temperatures below 850°C.