静电纺丝法制备超细聚苯乙烯纳米纤维

采用静电纺丝方法制备了超细聚苯乙烯纤维, 通过向溶液中添加有机胺盐并降低溶液浓度将纤维的平均直径降至100 nm, 并研究了盐的添加量对纤维直径的影响.

Ultrafine Polystyrene Nanofibers Prepared by Electrospinning

Ultrafine polystyrene(PS) nanofibers were prepared via the simple electrospinning technique.Uniform and smooth PS nanofibers were obtained with adding the organic salt BTEAC into the PS solutions and adjusting the concentration of PS solutions.Without the addition of BTEAC,PS fibers with few beads could be achieved with a PS mass fraction of 20%,and the average diameter of the fibers was 280 nm.The addition of the organic salt BTEAC could lower the critical concentration for the fiber formation and reduce the amount of beads on the fibers.Unltrafine PS fibers without any beads were obtained with a PS mass fraction of 10% and an ionic salt mass fraction of 0.5%.The average diameter of the fiber was successfully reduced to 100 nm.The influence of the salt concentration on the morphology and diameter of the PS fibers was also investigated.The viscosity and surface tension changes were measured with changing the concentration of BTEAC.The results show that the changes were so small that these factors could be ignored.It was suggested that variations of the fiber diameter should be mainly resulted from the changes of conductivity and conformation of the polymer chain as the concentration of BTEAC is varied.