Dilute solution properties of a polyurethane. I. Linear polymers

A linear polyurethane of high molecular weight was prepared in solution by the polyaddition of equimolar amounts of ethylene glycol and methylene bis(4-phenyl isocyanate). The polymer was fractionated by using a direct sequential extraction procedure, with a solvent–nonsolvent system consisting of N,N′-dimethylformamide (DMF) and acetone (A). The resulting fractions were characterized by viscosity and lightscattering measurements. The relationship between the intrinsic viscosity and molecular weight was found in DMF at 25°C. to be [η] = 3.64 × 10^?4M^0.71. The unperturbed polymer chain dimensions were determined from intrinsic viscosity measurements carried out under experimentally determined theta conditions.