Effect of TiO2/Al2O3 film coated diamond abrasive particles by sol-gel technique |
|
| Authors: | Weida HuLong Wan Xiaopan LiuQiang Li Zhiqi Wang |
| Affiliation: | a College of Materials Science and Engineering, Hunan University, Changsha, Hunan 410082, People's Republic of China b School of Science, Hunan University of Technology, Zhuzhou, Hunan 412008, People's Republic of China |
| Abstract: | The diamond abrasive particles were coated with the TiO2/Al2O3 film by the sol-gel technique. Compared with the uncoated diamonds, the TiO2/Al2O3 film was excellent material for the protection of the diamonds. The results showed that the incipient oxidation temperature of the TiO2/Al2O3 film coated diamonds in air atmosphere was 775 °C, which was higher 175 °C than that of the uncoated diamonds. And the coated diamonds also had better the diamond's single particle compressive strength and the impact toughness than that of uncoated diamonds after sintering at 750 °C. For the vitrified bond grinding wheels, replacing the uncoated diamonds with the TiO2/Al2O3 film coated diamonds, the volume expansion of the grinding wheels decreased from 6.2% to 3.4%, the porosity decreased from 35.7% to 25.7%, the hardness increased from 61.2HRC to 66.5HRC and the grinding ratio of the vitrified bond grinding wheels to carbide alloy (YG8) increased from 11.5 to 19.1. |
| Keywords: | Diamond Sol-gel TiO2 Al2O3 Vitrified bond |
| 本文献已被 ScienceDirect 等数据库收录！ | |