Effect of TiO2/Al2O3 film coated diamond abrasive particles by sol-gel technique

The diamond abrasive particles were coated with the TiO₂/Al₂O₃ film by the sol-gel technique. Compared with the uncoated diamonds, the TiO₂/Al₂O₃ film was excellent material for the protection of the diamonds. The results showed that the incipient oxidation temperature of the TiO₂/Al₂O₃ film coated diamonds in air atmosphere was 775 °C, which was higher 175 °C than that of the uncoated diamonds. And the coated diamonds also had better the diamond's single particle compressive strength and the impact toughness than that of uncoated diamonds after sintering at 750 °C. For the vitrified bond grinding wheels, replacing the uncoated diamonds with the TiO₂/Al₂O₃ film coated diamonds, the volume expansion of the grinding wheels decreased from 6.2% to 3.4%, the porosity decreased from 35.7% to 25.7%, the hardness increased from 61.2H_RC to 66.5H_RC and the grinding ratio of the vitrified bond grinding wheels to carbide alloy (YG8) increased from 11.5 to 19.1.