Modeling oxidation damage of continuous fiber reinforced ceramic matrix composites

For fiber reinforced ceramic matrix composites(CMCs),oxidation of the constituents is a very important damage type for high temperature applications. During the oxidizing process,the pyrolytic carbon interphase gradually recesses from the crack site in the axial direction of the fiber into the interior of the material. Carbon fiber usually presents notch-like or local neck-shrink oxidation phenomenon,causing strength degradation. But,the reason for SiC fiber degradation is the aw growth mechanism on its sur...