Thermal conductivity of vitreous sodium phosphates

Summary The thermal conductivity was measured for vitreous sodium phosphates of a variety of compositions in the temperature range from 50° to 160°. The temperature coefficient of the thermal conductivity decreases with the increase ofR (Na₂O/P₂O₅ mole ratio), and changes its sign from positive to negative at the value ofR near unity. In the composition range fromR=0.7 toR=1.4, where the thermal conductivity increases with the increase ofR, the composition dependence of thermal conductivity can be explained by the composition dependences of density and of compressibility. The residual water in the phosphates on the ultraphosphate side of composition seems to have some large effect on the thermal conductivity.

---

Zusammenfassung Die thermische Leitfähigkeit für glasige Natriumphosphate verschiedener Zusammensetzung wurde im Temperaturbereich von 50 bis 160° gemessen. Der Temperaturkoeffizient thermischer Leitfähigkeit nimmt mit dem Anteil anR (Na₂O/P₂O₅ molares Verhältnis) zu und ändert sein Vorzeichen von positiven zum negativen Werten vonR in der Nähe von eins. Im Bereich der Zusammensetzung vonR=0,7 bisR=1,4, indem die thermische Leitfähigkeit mit Zunahme vonR zunimmt, läßt sich die Abhängigkeit von der Zusammensetzung für die thermische Leitfähigkeit durch die Abhängigkeit von Dichte und Kompressibilität von der Zusammensetzung erklären. Das restliche Wasser in den Phosphaten auf der Ultraphosphat-Seite der Zusammensetzung scheint einen großen Einfluß auf die thermische Leitfähigkeit zu haben.

---

---

With 7 figures and 1 table