VUV-UV excited luminescent properties of LnCa4O(BO3)3:RE (Ln=Y, La, Gd; Re=Eu, Tb, Dy, Ce)

Calcium lanthanide oxyborate doped with rare-earth ions LnCa₄O(BO₃)₃:RE³⁺ (LnCOB:RE, Ln=Y, La, Gd, RE=Eu, Tb, Dy, Ce) was synthesized by the method of solid-state reaction at high temperature. Their fluorescent spectra were measured from vacuum ultraviolet (VUV) to visible region at room temperature. Their excitation spectra all have a broadband center at about 188 nm, which is ascribed to host absorption. Using Dorenbos’ and Jφrgensen's work P. Dorenbos, J. Lumin. 91 (2000) 91, R. Resfeld, C.K. Jφrgensen, Lasers and Excite States of Rare Earth M], Springer, Berlin, 1977, p. 45], the position of the lowest 5d levels E(Ln,A) and charge transfer band E_ct were calculated and compared with their excitation spectra.Eu³⁺ and Tb³⁺ ions doped into LnCOB show efficient luminescence under VUV and UV irradiation. In this system, Ce³⁺ ions do not show efficient luminescence and quench the luminescence of Tb³⁺ ions when Tb³⁺ and Ce³⁺ ions are co-doped into LnCOB. GdCOB doped with Dy³⁺ shows yellowish white light under irradiation of 254 nm light for the reason that Gd³⁺ ions transfer the energy from itself to Dy³⁺. Because of the existence of Gd³⁺, the samples of GdCOB:RE³⁺ show higher excitation efficiency than LaCOB:RE³⁺ and YCOB:RE³⁺, around 188 nm, which indicates that the Gd³⁺ ions have an effect on the host absorption and can transfer the excitation energy to the luminescent center such as Tb³⁺, Dy³⁺ and Eu³⁺.