Radical‐initiated polymerization of β‐methyl‐α‐methylene‐γ‐butyrolactone

β‐Methyl‐α‐methylene‐γ‐butyrolactone (MMBL) was synthesized and then was polymerized in an N,N‐dimethylformamide (DMF) solution with 2,2‐azobisisobutyronitrile (AIBN) initiation. The homopolymer of MMBL was soluble in DMF and acetonitrile. MMBL was homopolymerized without competing depolymerization from 50 to 70 °C. The rate of polymerization (R_p) for MMBL followed the kinetic expression R_p = AIBN]^0.54MMBL]^1.04. The overall activation energy was calculated to be 86.9 kJ/mol, k_p/k_t^1/2 was equal to 0.050 (where k_p is the rate constant for propagation and k_t is the rate constant for termination), and the rate of initiation was 2.17 × 10^?8 mol L^?1 s^?1. The free energy of activation, the activation enthalpy, and the activation entropy were 106.0, 84.1, and 0.0658 kJ mol^?1, respectively, for homopolymerization. The initiation efficiency was approximately 1. Styrene and MMBL were copolymerized in DMF solutions at 60 °C with AIBN as the initiator. The reactivity ratios (r₁ = 0.22 and r₂ = 0.73) for this copolymerization were calculated with the Kelen–Tudos method. The general reactivity parameter Q and the polarity parameter e for MMBL were calculated to be 1.54 and 0.55, respectively. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 1759–1777, 2003