Biodegradable polymers based on renewable resources. VII. Novel random and alternating copolycarbonates from 1,4:3,6‐dianhydrohexitols and aliphatic diols

Novel copolycarbonates containing 1,4:3,6‐dianhydro‐D ‐glucitol or 1,4:3,6‐dianhydro‐D ‐mannitol units, with various methylene chain lengths, were synthesized by bulk and solution polycondensations, of several combinations of carbonate‐modified sugar derivatives and aliphatic diols. Bulk polycondensations of 1,4:3,6‐dianhydro‐2,5‐bis‐O‐(phenoxycarbonyl)‐D ‐glucitol or 1,4:3,6‐dianhydro‐2,5‐bis‐O‐(phenoxycarbonyl)‐D ‐mannitol with four α,ω‐alkanediols having methylene chain lengths of 4, 6, 8, and 10, respectively, at 180 °C afforded the corresponding copolycarbonates with number‐average molecular weight (M_n) values up to 19.₂ × 10³. ¹³C NMR analysis disclosed that these polymers had scrambled structures in which the sugar carbonate and aliphatic carbonate moieties were nearly randomly distributed along a polymer chain. However, solution polycondensations between 1,4:3,6‐dianhydro‐2,5‐bis‐O‐(p‐nitrophenoxycarbonyl)‐D ‐glucitol or 1,4:3,6‐dianhydro‐2,5‐bis‐O‐(p‐nitrophenoxycarbonyl)‐D ‐mannitol, and the α,ω‐alkanediols in sulfolane or dimethyl sulfoxide at 60 °C gave well‐defined copolycarbonates having regular structures consisting of alternating sugar carbonate and aliphatic carbonate moieties with M_n values up to 33.₈ × 10³. Differential scanning calorimetry demonstrated that all the copolycarbonates were amorphous with glass‐transition temperatures ranging from 1 to 65 °C, which decreased with increasing lengths of the methylene chain of the aliphatic diols. Additionally, all the copolycarbonates were stable up to 310–330 °C as estimated by thermogravimetric analysis. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2312–2321, 2003