Crystal structure,dielectric properties of (K0.5Na0.5)NbO3 single crystal grown by flux method using B2O3 flux

Lead free piezoelectric single crystals of sodium potassium niobate (K_0.5Na_0.5)NbO₃ (KNN) were grown by high‐temperature solution method using two different fluxes; one with a mixture of NaF and KF and other with addition of B₂O₃ along with the mixture. In the present study, the growth of KNN crystals without B₂O₃ flux and the same with B₂O₃ flux were compared. It was found that additions of small amounts of B₂O₃ lowered the melting temperature of the solid solution and enabled better dielectric properties. Phase analysis showed that all samples were crystallized in pure orthorhombic perovskite phase. AFM morphological studies showed that the addition of B₂O₃ flux increased the roughness of the grown crystal. Further, addition of B₂O₃ flux slightly decreased the orthorhombic to tetragonal phase transition temperature T_(O—T) and the Curie temperature T_C. The ferroelectric behaviour of KNN single crystal has been investigated at room temperature. The crystal grown using B₂O₃ flux exhibited a remanent polarization (P_r) ～ 32 μC/cm² and coercive field (Ec) of ～11.8 kV/cm whereas the crystal grown without the use of B₂O₃ flux had a remanent polarization (P_r) ～ 36 μC/cm² and coercive field (Ec) of ～14.6 kV/cm.