Epitaxial growth of the CoFe2O4 film on SrTiO3 and its characterization |
| |
| Authors: | W Huang LX Zhou HZ Zeng XH Wei J Zhu Y Zhang YR Li |
| |
| Institution: | aState key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu 610054, China |
| |
| Abstract: | Cobalt ferrite (CoFe2O4) thin film is epitaxially grown on (0 0 1) SrTiO3 (STO) by laser molecular beam epitaxy (LMBE). The growth modes of CoFe2O4 (CFO) film are found to be sensitive to laser repetition, the transitions from layer-by-layer mode to Stranski–Krastanov (SK) mode and then to island mode occur at the laser repetition of 3 and 5 Hz at 700 °C, respectively. The X-ray diffraction (XRD) results show that the CFO film on (0 0 1) SrTiO3 is compressively strained by the underlying substrate and exhibits high crystallinity with a full-width at half-maximum of 0.86°. Microstructural studies indicate that the as-deposited CFO film is c-oriented island structure with rough surface morphology and the magnetic measurements reveal that the compressive strained CoFe2O4 film exhibits an enhanced out-of-plane magnetization (190 emu/cm3) with a large coercivity (3.8 kOe). |
| |
| Keywords: | A3 Epitaxial growth A3 Laser molecular beam epitaxy A3 Thin film B1 CoFe2O4 B2 Magnetic properties |
| 本文献已被 ScienceDirect 等数据库收录！ |