Raman scattering in Ag-intercalated TiS2

Ag-intercalated TiS₂ has been investigated using electron diffraction and Raman scattering. The energies of the E_g-1 and A_1g modes in 1T-TiS₂ at 300 K were found to be 232 and 336 cm^-1, respectively. In Ag_0.3TiS₂, at an ambient temperature of 4.2 K, modes were observed at 207, 239, 277, 311, and 347 cm^-1. Three of these modes have been associated with the formation of a superlattice at low temperatures. The superlattice formation was observed by electron diffraction and is attributed to an ordering of the silver atoms at interlayer interstices.