Crystal structure,thermal expansion and magnetic properties of Nd2Cu0.8Ge3 compound

A new ternary intermetallic compound, Nd₂Cu_0.8Ge₃, was synthesized and its crystal structure was determined by Rietveld refinement of X-ray powder diffraction data. The Nd₂Cu_0.8Ge₃ compound crystallizes in space group I4₁/amd (No. 141), with a tetragonal a-ThSi₂ structure type, and a=0.41783(2) nm, c=1.43689(9) nm, Z=2 and D_calc=7.466 g/cm³. Using the high temperature powder X-ray diffraction (HTXRD) technique, the lattice thermal expansion behavior of the compound was investigated in the temperature range of 298–648 K, and the result shows that its unit-cell parameters increased anisotropically when temperature increased. The magnetic susceptibility measured in the temperature range of 5–300 K indicated antiferromagnetic order of Nd₂Cu_0.8Ge₃ at low temperatures, and the magnetic susceptibility can be well described over the range of 50–300 K using Curie–Weiss law. The calculated effective magnetic moment (μ_eff) is 3.53 μ_B and dominated by the contribution of the Nd³⁺ ions.