Microstructure evolution of laser solid forming of Ti-Al-V ternary system alloys from blended elemental powders |
| |
| Authors: | Hua Tan Fengying Zhang Jing Chen Xin Lin and Weidong Huang |
| |
| Institution: | 1 State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, China 2 School of Materials Science and Engineering, Chang’an University, Xi’an 710064, China |
| |
| Abstract: | Morphology evolution of prior β grains of laser solid forming (LSF) Ti-xAl-yV (x 11,y 20) alloys from blended elemental powders is investigated. The formation mechanism of grain morphology is revealed by incorporating columnar to equiaxed transition (CET) mechanism during solidification. The morphology of prior β grains of LSF Ti-6Al-yV changes from columnar to equiaxed grains with increasing element V content from 4 to 20 wt.-%. This agrees well with CET theoretical prediction. Likewise, the grain morphology of LSF Ti-xAl-2V from blended elemental powders changes from large columnar to small equiaxed with increasing Al content from 2 to 11 wt.-%. The macro-morphologies of LSF Ti-8Al-2V and Ti-11Al-2V from blended elemental powders do not agree with CET predictions. This is caused by the increased disturbance effects of mixing enthalpy with increasing Al content, generated in the alloying process of Ti, Al, and V in the molten pool. |
| |
| Keywords: | |
| 本文献已被 CNKI 维普 等数据库收录！ |
|