| Abstract: | An evaluation method was proposed for resin impregnation using resin transfer molding of unsaturated polyester matrix composites with silane-treated glass cloth. The determination of whitening of the composite was carried out as a parameter of incompleteness of resin impregnation. The change of whitening with silane concentration was compared with the bending modulus as a parameter of chemical reinforcement. The materials used were unsaturated polyester resin as a matrix and methacryloxypropyltrimethoxysilane as a silane coupling agent for glass cloth. Resin transfer molding was used to produce four plies of glass cloth laminates by impregnating the resin. The silane-treated glass cloth repressed whitening above 0.026 w/w% of silane in aqueous solution, while the chemical reinforcement due to silane gave no appearance below 0.2 w/w% based on the bending test of the laminates. The large difference between the concentrations suggested that silane has a couple of functions, that is, chemical reinforcement and physico-chemical resin wettability. |