Kinetics of thermo-oxidative and thermal degradation of poly(d,l-lactide) (PDLLA) at processing temperature |
|
| Authors: | Xiaobo Liu Yaobang Zou Wenting Li Wenjin Chen |
| Institution: | a Institute of Microelectronic and Solid State Electronic, Department of Applied Chemistry, University of Electronic Science and Technology of China, Jianshe Beilu, Chengdu, Sichuan 610054, China b Chengdu Institute of Organic Chemistry, Chinese Academy of Sciences, Chengdu 610041, China c Sichuan Pushi Plastics and Rubber Co. Ltd, Yibin 644000, China |
| Abstract: | Poly(d,l-lactide) (PDLLA) degraded at processing temperature under air and nitrogen. A random chain scission model was established and used to determine the activation energy Ea, and FT-IR, 1H and 13C NMR were used to elucidate the degradation behavior under different atmospheres. Results showed that there were two to three stages. The 1st stage was dominated by the oligomers containing carboxylic acid groups and hydroxyl groups, during which oxygen and nitrogen had little effect on the degradation, thus they share similar Ea. When the oligomers were consumed over or evaporated, the 2nd stage began, and oxygen had a promoting effect on the thermo-oxidation process, resulting in the great decrease in Ea. The third stage of PDLLA was observed when it degraded under nitrogen over 200 °C, which was caused by the appearance of carboxylic acid substance. |
| Keywords: | Thermo-oxidation Thermal degradation Kinetics d" target="_blank">Poly(d l-lactide)" target="_blank">l-lactide) |
| 本文献已被 ScienceDirect 等数据库收录！ | |